Method and system for lining a tubular

ABSTRACT

A liner having an outer surface coated with a fluid absorbing coating is cladded to a tubing string by inserting the folded liner into the tubing string and then unfolding the liner against the tubing string. The liner may be a long single thin foil corrosion resistant liner coated with a sticky glue and a hygroscopic and/or other fluid absorbing coating to absorb fluid pockets trapped between the tubing and liner and inhibit corrosion and leakage of, the elongate tubing string.

CROSS-REFERENCE TO RELATED APPLICATIONS

The present application is a continuation of U.S. patent applicationSer. No. 15/121,468, filed on Aug. 25, 2016, which is a National Stage(§ 371) of International Application No. PCT/EP2015/054115, filed Feb.27, 2015, which claims priority from European Application No.14157013.5, filed Feb. 27, 2014, the disclosures of each of which arehereby incorporated by reference in their entirety.

BACKGROUND OF THE INVENTION

The invention relates to method and system for internally lining atubing string to protect the tubing string against corrosion and/orleakage.

Wellbores for the exploration and production of oil, gas or otherminerals from subterranean reservoir layers are typically provided withprotective tubing, casing and/or other liner strings. These may includea pipe string lowered into an openhole section of the wellbore andcemented in place. Herein, the term casing is typically used to indicatea pipe string extending from surface into the wellbore, whereas linermay typically be used to indicate a pipe string which extends from adownhole location further down the wellbore. Hereinafter, the termcasing will be primarily used, but the invention is equally applicableto liner.

The casing or liner strings may be designed to withstand a variety offorces, such as collapse, burst, and tensile failure, as well aschemically aggressive brines. The casing string is typically assembledfrom multiple interconnected pipe sections, having a length of forinstance about 10 metres each. Casing connections connect adjacent pipesections. The casing sections may be fabricated with male threads oneach end, wherein shorter-length casing couplings with female threadsare used to join the individual sections of casing together.Alternatively, pipe sections may be fabricated with male threads on oneend and female threads on the other.

Casing may be run to protect fresh water formations, isolate a zone oflost returns or isolate formation layers with significantly differentpressure gradients. The operation during which the casing is put intothe wellbore is commonly called “running pipe.”

Inside the innermost casing, a wellbore may typically be provided withanother tubing string, typically referred to as production string orproduction tubing. Herein, the production tubing may be assembled withother completion components to make up the production string. Theproduction string is the primary conduit through which reservoir fluidsare produced to surface. The production string is typically assembledwith tubing and completion components in a configuration that suits thewellbore conditions and the production method. The tubing itself may bemade up from interconnected pipe sections, in a similar fashion to thecasing strings. An important function of the production string is toprotect the primary wellbore tubulars, including the casing and liner,from corrosion or erosion by the reservoir fluid.

Interior surfaces of the production tubing and their associatedconnections are frequently subjected to one or more of relatively hightemperatures, high pressures and highly corrosive fluids. Temperaturesmay range up to 175° C. or more. Pressures may be as high as 1400 barsor more. The reservoir fluids may be highly corrosive, for instance dueto the combination of hydrocarbons, CO₂ and/or H₂S in the presence ofwater. The use of secondary and tertiary enhanced recovery methods inhydrocarbon production, such as gas injection, water flooding andchemical flooding, may further aggravate the situation.

Pipe sections for wellbore tubulars, including the casing or productiontubular, are usually manufactured from plain carbon steel with varyingcompositions that is heat-treated to varying strengths. Alternatively,pipe sections may be specially fabricated of stainless steel, nickelalloys, aluminum, titanium, fiberglass and other materials.

Materials have different resistance to corrosion. Carbon steel forinstance is relatively inexpensive, but also more prone to corrosionthan the other materials listed above.

Several types of corrosion mechanisms exist, including:erosion-corrosion (also known as impingement), stress corrosioncracking, sulphide stress cracking, pitting, and galvanic corrosion.

Corrosion in metals may be caused by the flow of electricity from onemetal to another metal or from one part of the surface of one piece ofmetal to another part of the same metal where conditions permit the flowof electricity. Further, a moist conductor or electrolyte must bepresent for this flow of energy to take place. Energy passes from anegative region to a positive region via the electrolyte media.

Electrical contact or coupling of dissimilar metals frequently causesincreased corrosion. This form of corrosion is generally referred to asgalvanic corrosion. Galvanic corrosion is quite prevalent andtroublesome, occurring in a wide variety of circumstances. For example,coupling aluminum and iron pipe together will result in very rapidcorrosion of the aluminum pipe section. The galvanic corrosion mechanismmay be illustrated by considering the effect of electrically connectingzinc to platinum immersed in sea water. Under these conditions, theplatinum is inert and does not corrode, while the zinc is attacked. Thereactions occurring on the surface of the zinc are the anodic oxidationof zinc to zinc ions, and the cathodic reduction of dissolved oxygen tohydroxide ions. If the electrical potentials of these two metals aremeasured, the platinum would be found to have a positive potential,while the zinc would be found to have a negative potential. As may beappreciated, as the potential difference increases, galvanic corrosionincreases.

Obviously, from a corrosion standpoint, the replacement of steeltubulars and associated hardware with materials less subject tocorrosion would be highly desirable in gas and oil applications, if itwere practical or economically viable. Non-metallic components, such asfiberglass casing, tubing, sucker rods and the like are finding theirway into oil field applications. Performance limitations, includingservice loads, pressures and temperatures, restrict the across-the-boardreplacement of metallic hardware, however. On the other hand, pipesections made of solid corrosion resistant alloy (CRA), such asstainless steel and nickel alloy, may provide sufficient corrosionresistance. But tubular sections made of solid corrosion resistantalloys are typically much more expensive than carbon steel. The lattermay render projects uneconomical. In addition, newly developedhydrocarbon reservoirs are producing increasingly corrosivehydrocarbons, for instance including a greater percentage of H₂S,requiring higher grade Corrosion Resistant Alloys (CRAs). And highergrade CRAs are increasingly more expensive. For instance, compared toAPI grade P110 carbon steel, the same pipe section made of CRA may be upto 5, 10 or even 25 times more expensive (when made of 316L,SM25CRW-110/125, or C22 CRA respectively).

Several manufacturing methods have been developed for producingcorrosion resistant clad or lined carbon steel tubular, for instance fortransporting oil and gas, to achieve economic advantages over solidcorrosion resistant alloy (CRA) tubular such as stainless steel andnickel alloy. However, the use of these clad or lined tubulars has notgained acceptance for downhole tubular primarily due to the lack of athread connection that has demonstrated adequate corrosion resistanceperformance.

To guard against galvanic corrosion, insulating coatings may be applied.In order for a coating to be used on tubular sections and threadedcouplings to protect the metal substrate from corrosion, the coatingmust be resistant to attack and maintain its adherence to the metalsubstrate under the harsh downhole conditions referred to above.

In various oil and gas applications, steel pipe is provided with alining of corrosion-resistant material. For example, it is known to bondvarious epoxy-based coatings to the interior of the pipe, as well ascoatings containing polyethylene, polyvinyl chloride and otherthermoplastic and thermosetting materials.

Of the various polymeric coating materials, arylene sulfide polymershave gained wide acceptance, see for instance U.S. Pat. No. 3,354,129.Generally, these polymers consist of a recurring aromatic structurecoupled in repeating units through a sulfur atom. Commercially availablearylene sulfide polymers which have been used for coating oil and gaspipes and pipe couplings are polyphenylene sulfides. The polyphenylenesulfides used in oil and gas applications exhibit high melting points,outstanding chemical resistance, thermal stability and arenon-flammable. They are also characterized by high stiffness and goodretention of mechanical properties at elevated temperatures as well asthe ability to deform smoothly, thereby, for example, preventing thegalling of threads, even at high thicknesses.

U.S. Pat. No. 3,744,530 describes polyphenylene sulfide coated pipes,wherein the polyphenylene sulfide coating also contains a filler, suchas iron oxide, in an amount of between 5% to 30%.

While polymeric coated pipes and couplings have gained wide acceptancein applications requiring corrosion protection, the cracking of suchcoatings during installation and in use tends to limit their insulatingeffect, increasing the likelihood that galvanic corrosion will takeplace. This is particularly relevant in the female part or pin-end ofthe connections, where cracking may occur during assembly of theconnection. Moreover, the polymeric coatings of threaded couplings areparticularly prone to cracking due to the stresses imparted duringassembly of connections. In addition to cracking, many polymers allowdiffusion of hydrogen and other light hydrocarbons through the thicknessof the coating or liner, thereby allowing gas to accumulate betweenlayers, which, in the case of a corrosion resistant liner could resultin collapse if the pressures in the bore and annulus become unbalanced.

JP 60 109686 A (KAWASAKI HEAVY IND LTD) 15 Jun. 1985 (1985 Jun. 15)provides a pipe system for transport of corrosive fluids. The pipesystem comprises a tubular member made of a corrosion prone metal. Eachtubular member is provided with an inner lining of a corrosion resistantmaterial. At each end, the tubular member and the inner lining areconnected to a threaded coupling member, which is made of a corrosionresistant material. The tubular member and the liner are connected tothe threaded coupling member by a weld seam. But the welding of solidCRA couplings to a carbon steel pipe body, or the welding relatedmethod, can cause issues in itself. See for instance the description ofgalvanic corrosion above. In addition, the cost saving from using cladsteel rather than solid CRA is particularly valid when the total wallthickness of the pipe increases. When the product of outer diameter (OD)times wall thickness (T) decreases however, the cost benefit ofcorrosion resistant alloy clad pipe versus solid CRA pipe decreasesrapidly. For instance, for pipe clad with Incoloy 825, the cost benefitis reduced to nil for tubulars having smaller OD×T. The latter howeverare typically used for production tubing.

While the use of corrosion resistant alloys for corrosion control hasdemonstrated superior corrosion resistance properties, they are quitecostly and exhibit complex manufacturing and handling constraints. Theprice of high-performance steel, such as 18-8 stainless steel, may beabout 5 times as expensive as carbon steel. Nickel alloys for instance,which may also include high percentages of chromium (e.g. more than 10%)and/or molybdenum, may exceed the price of carbon steel with a factor ofabout 20 to 30. Nickel alloys, however, are often the material of choicein environments containing relatively large volumes of H₂S. Forinstance, when the H₂S partial pressure exceeds 5 to 10 bars, nickelalloys may be required.

In oilfield applications, polymeric coatings will be unsuitable when thepartial pressures of either CO₂, H₂S and/or water exceed a certainthreshold, as these materials may permeate through the polymericcoating, which may lead to corrosion of the carbon steel base material.Also, the temperature range wherein polymeric coatings can be applied istypically limited to a maximum of about 100 to 150 degree C.

US-2007/0095532 discloses an apparatus to deploy a patch comprising aninner metal tube and an outer resilient sealing member. Suitably, theinner metal tube is formed from steel, preferably, carbon steel. Theouter resilient sealing member is formed from an elastomeric material.Suitably, the patch may be from 10 to 1000 feet in length.

As a disadvantage, in the disclosure of US-2007/0095532, the length ofthe liner patch is inherently limited by the apparatus described. Theliner patch is clamped by extending and retracting slips attached to theapparatus, so the weight of the liner patch is carried by the frictionthese slips exert on the liner. The force applied by these slipsdetermines the frictional force. The extending and retracting slips willhave insufficient capacity to support liner exceeding a certain length,such as several kilometres. Furthermore, in the case of a very thinliner, the pressure that the slips can exert before deforming the lineris minimal, minimizing the friction force also. Although a thin liner islighter than a thicker patch, the weight of the liner is still typicallyin the order of 1.3 kg/m. This would provide a total weight of severalthousand kilograms if one would consider lining the production tubingalong the length of the wellbore.

As hydrocarbon wellbores extend to ever greater target depths, forinstance in the range of five to ten kilometres or even more, theapparatus of US-2007/0095532 would be unsuitable to provide a linerpatch to the entire inner surface of the production tubing.

Furthermore, the apparatus of US-2007/0095532 is supported by a wirelinewhich, in the configuration as disclosed, would have to travel throughthe liner. For longer lengths, the practicalities of threading severalkilometres of wireline through the liner patch, while still supportingthe weight of the liner by the wire line while running into the well,are unrealistic. This is supported by the exemplary length of linerpatch as disclosed in US-2007/0095532, which is limited to 1000 feet(about 300 metres).

US-2010/0247794-A1 wellbore tubing lining method wherein a polymer layeris cured downhole actinic radiation. The liner is introduced in theborehole via an apparatus attached to a wireline, which would thanexpand the liner via a vessel or bladder on a wire line. The bladderwill inflate along the full length of the liner to expand the liner. Thesystem is limited to the delivering of a polymer liner. Also, the systemcan only be applied for limited lengths. The fabrication of a bladder orvessel to expand the liner will inherently limit the length of the linerto be expanded. Providing a bladder which extends along the entirelength of the production tubing will be impossible. Moreover, thenecessity to run such a vessel into the hole will further limit themaximum length thereof.

U.S. Pat. No. 3,785,193 discloses a liner expanding apparatus and amethod including lowering and affixing a liner by means of wireline. Theliner is crimped onto an expansion tool and hangs down from it. Thisconfiguration has similar limitations to patent documentsUS-2007/0095532 and US-2010/0247794-A1 described above, in that theclamping of the liner is based on friction. The friction is insufficientfor longer lengths of liner, particularly for thinner liner, given thelimited frictional force which can be generated. Also, given that theapparatus is suspended from a wireline, running in the liner will proveimpossible above a certain threshold length of liner, due to problems atthe surface. As a result, the system of U.S. Pat. No. 3,785,193 isunsuitable to line production tubing along its entire length, which maybe in the order of several kilometres.

Other methods and system for expanding a liner within a surroundingtubular string are disclosed in International patent application WO98/21444 and US patent applications US 2006/052936, US2007/095532 and US2010/247794.

A general problem with the known tubing lining systems and methods isthat pockets of fluids may be trapped between the liner and tubing,which may result in detachment of the liner from the inner wall of thetubing and collapse of the liner.

There is a need for an improved method and system to protect tubularsagainst corrosion and leakage by use of a tubing liner assembly thatautomatically removes fluid from the residual space between the linerand tubing, thereby inhibiting formation of fluid pockets and/orlongitudinal leakage paths between the liner and tubing and reducing therisk of detachment of the liner from the inner surface of the tubing andthe associated risk of subsequent collapse of the liner.

SUMMARY OF THE INVENTION

The present invention therefore provides a method for lining a tubingstring, comprising;

-   -   inserting a folded liner having an outer surface which is at        least partially coated with a fluid absorbing coating into the        tubing string;    -   unfolding the liner to expand the liner against an inner surface        of the tubing string; and    -   inducing the coating to absorb fluid trapped between an inner        surface of the tubing string and an outer surface of the        expanded liner.

The coating may comprise bonding and liquid absorbing additives, such asa sticky glue and a hygroscopic material, such as silica gel and/or across-linked acrylate polymer described in U.S. Pat. No. 7,144,980,which is generally known as a Super Absorbent Polymer (SAP) or hydrogel,which absorbs any substantial pockets of water and/or other fluidtrapped, and thereby enhances the bond, between the tubing string andthe expanded liner.

In accordance with another aspect of the invention there is provided asystem for lining a tubing string in a wellbore, comprising a liner,which is configured to be folded in a collapsed state into the tubingstring and to be unfolded against an inner surface of the tubing stringand which is at least partially coated with a fluid absorbing coatingthat is configured to absorb fluid trapped between the inner surface ofthe tubing string and the expanded liner.

The method and system according to the invention enable continuouscladding of a kilometres long oil and/or gas well tubing and/or casingstring by a single thin foil corrosion resistant liner that may becoated with hygroscopic and sticky glue to enhance the bonding of theliner to, and inhibit corrosion and leakage of, the tubing and/or casingstring.

These and other features, embodiments and advantages of the method andsystem according to the invention are described in the accompanyingclaims, abstract and the following detailed description of non-limitingembodiments depicted in the accompanying drawings, in which descriptionreference numerals are used which refer to corresponding referencenumerals that are depicted in the drawings.

Similar reference numerals in different figures denote the same orsimilar objects. Objects and other features depicted in the figuresand/or described in this specification, abstract and/or claims may becombined in different ways by a person skilled in the art.

BRIEF DESCRIPTION OF THE DRAWINGS

The invention will be described hereinafter in more detail and by way ofexample with reference to the accompanying drawings, in which:

FIG. 1 shows a perspective view of separate layers of a liner accordingto the invention;

FIG. 2 shows a perspective view of separate layers of a liner accordingto the invention;

FIG. 3 shows a perspective view of an embodiment of a liner of theinvention;

FIG. 4 shows a perspective view of an embodiment of a liner according tothe present invention;

FIG. 5 shows a perspective view of another embodiment of a lineraccording to the present invention;

FIG. 6 shows a perspective view of a practical embodiment of the linerof the invention;

FIG. 7 shows a perspective view of a reel comprising the liner accordingto the invention;

FIG. 8 shows a perspective view of a cross section of a tubular, whichin a first step is provided with a liner according to the invention;

FIG. 9 shows a perspective view of a cross section of a tubular, whichin a second step is provided with a liner according to the invention;

FIG. 10 shows a perspective view of a cross section of a tubular, whichin a third step is provided with a liner according to the invention;

FIG. 11 shows a schematic cross section of a wellbore provided with aliner according to the invention;

FIGS. 12 to 19 show exemplary steps of various embodiments to fabricatethe composite material of the invention;

FIGS. 20 and 21 show respective embodiments of methods to manufacturethe composite liner of the invention;

FIGS. 22 to 24 show perspective views of respective methods tomanufacture a pipe using the composite liner;

FIGS. 25 to 27 show cross-sectional views of respective methods tomanufacture a pipe using the composite liner;

FIG. 28 shows a cross-section of an embodiment of a liner of theinvention arranged on wellbore tubing;

FIG. 29 shows an exemplary graph of a signal to monitor integrity of theliner;

FIGS. 30 to 32 show consecutive steps in an embodiment of a process tofabricate a liner of the invention;

FIG. 33 shows a cross section of an embodiment of a system of theinvention for introducing a liner in a wellbore;

FIG. 34 shows a perspective view of an embodiment of an expander for thesystem of the invention;

FIG. 35 shows a cross section of a wellbore provided with the system ofthe invention, as well as a step in introducing the liner in thewellbore;

FIGS. 36 to 39 show consecutive steps of an exemplary method for lininga wellbore tubular; and

FIG. 40 shows a perspective view of an embodiment of a method of lininga wellbore tubing according to the invention.

DETAILED DESCRIPTION OF DEPICTED EMBODIMENTS

FIG. 1 shows an embodiment of a composite material 10 suitable formanufacturing a thin foil liner according to the present invention. Thecomposite material comprises a first polymer layer 12, a second polymerlayer 14 and an intermediate metallic layer 16. Optionally, as shown inFIG. 2, a first adhesive layer 18 may be arranged between the firstpolymer layer and the metallic layer. A second adhesive layer 20 may bearranged between the metallic layer and the second polymer layer.

Herein, the first and/or second polymer layer may be a layer consistingof a single polymer or may itself be a composite layer. Each polymerlayer may in fact include steel, carbon, or glass fibre wire and/orparticles of a relatively hard material embedded in the polymer. Hardherein implies being harder or stronger than the polymer base material.The hard-particulate material may serve for abrasion protection on theinner diameter of the composite liner of the invention.

The respective layers of the composite material are bonded to eachadjacent layer, forming a layer of assembled composite material 10 asshown in FIG. 3. The assembled composite material may have any desirableform, such as a longitudinal strip.

FIGS. 4 and 5 show different examples of a method to form the compositematerial into a tubular shape. FIG. 4 shows the first polymer layer 12formed into a tubular shape. The metal layer 16 is provided in the formof a longitudinal strip 22 and bend around the tubular first polymerlayer 12. After bending, the sides 24 of the metal layer 16, whichextend in axial direction, are connected to each, for instance bywelding. In another embodiment, shown in FIG. 5, the metallic layer 16is provided in the form of longitudinal strip 22. Said strip 22 ishelically wound around the tubular first polymer layer 12. The sides 24of the strip 22 may be connected to each other, for instance by welding.Alternatively, the metallic layer may be glued to the polymer layer. Thesecond polymer layer 14 is applied in a similar fashion, providing alongitudinal tube 30 made of the composite material 10, see FIG. 6.

In an embodiment shown in FIG. 6, tool 32 may be used to model thelongitudinal tube 30 of composite material in a collapsed tubular 34,having a reduced outer diameter. Herein, the tool 32 may have createdone, two or more longitudinal folds 36 extending in axial direction.Said collapsed composite tube may have any suitable length and can bearranged on a reel 40, see FIG. 7. Alternatively, the compositematerial, or components thereof, may be manufactures as a collapsedtubular, rather than in the round shape and subsequently folded.

The collapsed tube 34 may be used to line a pipe 50. In a first step(FIG. 8), the collapsed tube 34 is arranged within the pipe 50. In asecond step (FIG. 9), the collapsed tube 34 is expanded, to a tubularform 30 (FIG. 10).

In a typical oilfield application (FIG. 11), a wellbore 60 may beprovided extending into a formation 62 below ground level 64. Thewellbore is typically provided with one or more tubular casings orliners, such as conductor pipe 66, intermediate casing 68 and productiontubing 70. Herein, the production tubing is typically included in aproduction casing, which is not shown however to improve clarity.Produced hydrocarbons will be transported to surface via the inside ofthe production tubing 70. Consequently, the inner surface of theproduction tubing 70 may be exposed to varying quantities of CO2 and H2Sin the presence of water, all of which may be transported to surfacetogether with the hydrocarbons.

In an embodiment, the collapsed tube 34 is unreeled and inserted thoughthe production tubing. Preferably, the tube 34 herein extends all theway to the downhole end 72 of the production tubing above a Side SlidingDoor (SSD) and/or a Side Pocket Mandrel (SPM) to be able to cover atleast a substantial part of the entire length thereof.

The collapsed tube 34 can for instance be inserted into the wellbore byconnecting a weight to the downhole end thereof and lowering said weightin the wellbore until it reaches the bottom. Alternatively, thecollapsed tube can be inserted in the wellbore by applying pressure, orby running it in as part of, or in fact around, a Coiled Tubing stringor other type of running string. The running string can be arrangedeither inside the collapsed composite tube 34, or even on the outsidethereof.

Subsequently, the collapsed tube 34 is expanded to its expanded state.Herein, the expanded tube 30 preferably has an outer diametercorresponding to or slightly larger than the inner diameter of thetubing 70, so that the outer surface of the expanded tube engages theinner surface of the tubing 70.

A problem with conventional cladding concepts is the continuity of thecladding layer, especially at the locations of the connections betweenrespective tubular sections. The composite liner of the invention can bemade in a factory and consequently the continuity can be thoroughlyinspected on surface before installation in the wellbore. To maintainthe integrity of the composite liner during insertion in the wellbore,the outer diameter of the composite liner may be provided withprotection means to protect against damage during running, installationor bonding to the inner surface of the wellbore tubing. Said protectionmeans may include wires comprising a relatively damage resistantmaterial arranged on the outer diameter of the composite liner. Thedamage resistant material may include one or more of steel, carbon, orglass fibre wires.

The collapsed tube 34 can be expanded in a number of ways. In a firstembodiment, the tube 34 can for instance be inflated with a pressurizedfluid in its interior. In this case, the downhole end of the tube 34 isclosed before inserting it in the wellbore. After insertion, the surfaceend is cut off, whereafter the pressurized fluid is introduced toinflate and expand the liner. In a second embodiment, an expander cone74, having a largest outer diameter which is substantially similar tothe inner diameter of the tubing 70, can be pushed or pulled through thecollapsed tube 34 to expand it. The expander can be moved from surfacetowards the downhole end 72 by pumping a pressurized fluid to push theexpander. Subsequently, while the tube is maintained in position by theweight mentioned above, an expander cone 74 can be pulled to surface toexpand the tube 34. Herein, a string, such as a coiled tubing string ora wireline, may have been integrated within the composite tube 30 duringmanufacturing thereof (not shown). The expander 74 may be attached to anend of said string or wireline before inserting the composite liner inthe wellbore. Subsequently, the expander may, for instance in acollapsed form, be lowered in the wellbore together with the liner. Whenthe composite liner is in the correct position, the expander cone may betransferred to its expanded form and pulled to surface using said stringor wireline. Alternatively, the expander can be propelled to surfaceusing hydraulic pressure generated by reverse circulating the well.

The expanded composite liner 30 may stick to the inner surface of thetubing 70 by various means. For instance, the outer surface of thecomposite liner may have been provided with an adhesive layer. Saidadhesive layer may be applied to the outer surface of the collapsedtubing 34 during insertion into the wellbore using an adhesiveapplicator device 76, which may include a spraying device or a rollerfor applying the adhesive. Said adhesive may include a heat activatedadhesive, which can be activated by introducing heated fluid into thewellbore or even by the elevated temperature in the wellbore, which asmentioned before are frequently in excess of 175° C. Alternatively, anactivator which will activate the adhesive can be injected in thedrilling fluid.

As shown in FIG. 12, in a first step of an exemplary embodiment forfabricating the composite material of the invention, strips of the firstpolymer layer 12, the metallic layer 16 and the second polymer layer 14are arranged on top of each other. Optionally, the adhesive layers 18,20 are interposed as shown in FIG. 2. The assembly of the stacked stripsis folded in a tubular form along the length thereof, as shown in FIG.4, until the opposite longitudinal sides 24, 25 of the metallic layer 16and the opposite longitudinal sides 80, 81 of the first polymer layerengage each other and are aligned. Herein, opposite longitudinal sides84, 85 of the second polymer layer leave a longitudinal opening 86 inbetween them, exposing the abutting sides 24, 25 of the metallic layer.The opening 86 may for instance expose about 1 to 20 mm, for instanceabout 10 mm, of the metallic strip on each side of said abutting sides24, 25.

In a next step, the sides 24, 25 of the metal layer 16 will be joined bywelding (schematically indicated by flash 88), for instance using arcwelding or laser welding or a combination of these two weldingtechniques, producing weld 90. The first polymer layer 12 may be heatedsimultaneously to a temperature exceeding the melting point of therespective polymer material by the heat produced while welding the metallayer, leading to polymer weld 92. To ensure the structural integrity ofthe welds 90, 92, mechanical force may be applied to ensure both sides24, 25 are engaged during the welding process.

As shown in FIG. 14, to fill the blank area 86 on the upper surface ofthe metal 16, an additional polymer strip 94 will be inserted in theopening 86, using a mechanical system. Said mechanical system may forinstance include a roller 96. To connect the strip 94 to the secondpolymer layer 14 and/or the metallic layer 16, heat can be applied usinga heat source 98 such as hot dry air, infrared, or microwave (FIG. 15).

In an alternative embodiment, sides 24, 25 of the metallic layer areengaged in a butt joining (FIG. 16) or lap joining (FIG. 17) fashion.Herein, openings 86, 100 exposes both the outside surface and the insidesurface of said sides 24, 25 respectively, which are subsequently joinedusing welding techniques, such as the techniques mentioned above,creating weld 90 (FIG. 18).

In a subsequent step (FIG. 19), the openings 86, 100 are provided, forinstance filled or spray coated, with polymer strips 94, 102respectively, as described above. An attachment device 104, for instancea heat source, may ensure bonding of the strip 102 to the metallic layer16.

Herein below, additional details of embodiments of the manufacturingprocess of the composite liner of the invention are described.

The liner may be fabricated as a composite strip, which can be made bythe following processes:

a) A thin metal strip laminated with a polymer film or a reinforcedpolymer film, either on one side or on opposite sides;

b) A polymer coated thin metal strip;

c) Polymer coating followed by winding of reinforcement fiber orreinforcement fiber fabric;

d) A combination of a), b) and c).

The first and/or second polymer layers can be applied only one side incomposite strip manufacturing process stage. The application of Polymerlayer for the other side can be applied in following pipe manufacturingprocesses.

To improve the bonding between metal strip and polymer film, adhesivescan be added.

The polymer film can fully or partially cover each side of the metalstrip according to the joining method of both longitudinal sides of themetal strip to make a pipe.

The composite strip can be made into a strip coil or continuously beconnected to next step, pipe manufacturing process

FIG. 20 shows first polymer film roll 112, second polymer film roll 114,metallic strip roll 116, and the optional first adhesive film roll 118and second adhesive film roll 120. The respective films are unrolled andjointly transferred through heating device 122. The heating device 122comprises for instance an induction heater, infrared (IR) heaterelements, microwave heating elements, or ultraviolet (UV) heatingelements. Subsequently, the films may be jointly led past compressiverollers 124, to improve bonding between the respective films. In a nextstep, the bonded films are cooled by cooling device 126, for instance byspraying a substance 128 such as compressed air or water. The bondedstrip of composite liner is rolled onto composite liner roll 130.

FIG. 21 shows another embodiment, wherein metallic strip roll 116 isunrolled. Adhesive coating devices 138, 140 subsequently apply the firstadhesive layer 18 and the second adhesive layer 20, for instance byspraying. In a next step, polymer coating devices 132, 134 apply thefirst polymer layer 12 and the second polymer layer 14, for instance byspraying. The assembled composite material 10 may subsequently betransferred through heating device 122, led past compressive rollers124, and cooled by cooling device 126. The bonded strip of compositeliner is rolled onto composite liner roll 130.

FIG. 22 shows an embodiment of a composite pipe manufacturing process.The composite liner roll 130 is unrolled. A strip of the composite linermaterial 10 is fed to a number of rollers 140-158, which continuouslyform, and bend said strip 10 in a tubular form 30, or maintain saidtubular form. In between rollers 152 and 158, the opposite sides of thestrip 10, indicated by sides 24, 25 of the metal layer 16, are bonded bywelding, as indicated by flash 88. Tool 32 collapses the tube to acollapsed tubular 34, having a reduced outer diameter and longitudinalfolds 36. The collapsed composite tube 34 is subsequently arranged onthe reel 40.

In the embodiment of FIG. 23, the first polymer film roll 112 isunrolled, providing the first polymer film 12. The rollers 140-158 formand bend the first polymer film 12 in tubular form, and the oppositesides 80, 81 of said film are bonded, for instance by welding asindicated by flash 88. A strip of metallic layer 16 is applied, byhelically winding said strip around the tubular first polymer layer 12.Thereafter, the second polymer layer 14 is applied by the polymercoating device 132. The assembled composite tube 30 is led past heatingdevice 122 to improve bonding between the respective layers and pastcooling device 126 for cooling. Subsequently, the composite tube 30 iscollapsed and arranged on the reel 40 (not shown).

In the embodiment of FIG. 24, the roll 130 is unrolled, providing astrip of composite liner material 10. The rollers 140-158 bend saidstrip in tubular form. Herein, the opposite sides of the strip,including all its respective layers, are bonded by welding 88.Subsequently, the composite tube 30 is collapsed and arranged on thereel 40 (not shown).

In general, the strip of composite material 10 can make it through thefollowing steps:

a) Uncoiling into strip of composite material;

b) Forming of said strip into tubular shape;

c) Joining opposite sides of tubular shaped strip;

d) Optionally, winding of a reinforcement fibre such as carbon fibre,glass fibre or reinforcement fibre fabric onto the outer surface of thecomposite tubular 30 and bonding it to the outer surface thereof;

e) Corrugated forming of the composite pipe 30; and

f) Coiling of pipe.

The above processes can be continuously progressed from a) to f), orbatch processes can be divided into several sub-groups, for instance:

Batch 1 process: from a) to d); and

Batch 2 process: e) and f).

FIG. 25 shows the welding of opposite sides 24, 25 of the metal layer 16by fusion welding. The first polymer layer 12 is heated to a temperatureexceeding the melting temperature of the polymer by the heat of thefusion welding, so that its sides 80, 81 are simultaneously joinedduring welding of the metal layer.

FIG. 26 shows the bonding of the sides 24, 25 of the metal layer 16 byfusion welding. The first polymer layer 12 is heated to a temperatureexceeding the melting temperature of the respective polymer by fusionwelding heat, and its sides 80, 81 are simultaneously joined duringwelding of the metal layer. The uncovered part 86 of the outer surfaceof the metal layer 16 is covered by a coating of a polymer or byattaching of polymer film 94. Subsequently, the area covered by thepolymer strip or coating 94 may be cooled followed by heating.

FIG. 27 shows the bonding of the sides 24, 25 of the metal layer 16 bylaser welding. The polymer material of the second polymer layer 14 istransparent for the laser beam, and is not heated by the laser beam.During welding of the metal layer 16 by the laser, the sides of theinner and outer polymer layers are heated by heat transferred from themetal layer, and bond as a result.

In a practical embodiment, the composite material of the presentinvention comprises a single combination of polymer-metal-polymerlayers. The composite material may have a total thickness in the rangeof about 150 μm to about 2 mm, typically about 1 mm or less. Eachpolymer layer in the polymer-metal-polymer composite material may be thesame.

In an embodiment, the first and second polymer layers have a thicknessin the range of about 50 μm to 500 μm. The polymer layers may comprise abase polymer selected from the group of thermoplastics such as PEEK(Polyetheretherketone), PI (polyimide), PPS (polyphenylene sulfide), PEI(poletherimide), PMMA (Polymethylmethachylate), PVDF (Polyvinylidenefluoride), PA (polyamide), PVC (Polyvinyl chloride), and PE(Polyethylene), and thermoset plastics such as expoxy, phenolic,melamine, unsaturated polyester, and polyurethane. Said base polymer maycomprise a reinforcement, which may be a mixture of one or more of:short carbon fibre, PTFE, Graphite, nano oxide particle having adiameter below 20 nm. The blend may comprise additives to improvebonding with the reinforcement.

The metal layer may have a thickness in the range of 50 μm to 500 μm.The metal may comprise one or more of aluminum (Al) alloy, nickel (Ni)alloy, titanium (Ti) alloy, stainless steel. To improve the bonding withthe polymer layers, if necessary, chemical treatment may be applied.

De-bonding is a major problem for conventional polymer clads in general.Well fluids may permeate into the polymer clad and expand when the wellcycles to a lower pressure, thus pushing the clad away from the wall ofthe carbon steel base pipe. This problem is specifically prevented inthe composite liner of the present invention, by including animpermeable metallic layer, preferably made of corrosion resistantalloy, between the wellbore fluids and the bonding agent on the outerdiameter of our composite liner clad. Also, the de-bonding problem canbe prevented on the inner diameter of the metallic layer, by making thepolymer layer on that side (e.g. the first polymer layer) fullypermeable, thus preventing pressure build-up.

As shown in FIG. 28, when the liner 34 is applied to the wellbore tubing70, the metal layer 16 of the liner 34 may at surface be electricallyconnected to the tubing 70. Electrical circuit 200 may includeelectrical wires 202, 204 and electrical measurement device 206. Thedevice 206 may be a volt meter, a current meter, or a resistivity meter.

FIG. 29 shows an exemplary output of the monitoring device 206 (y-axis)in time (x-axis). In a steady state, wherein the liner 34 is properlyapplied to the tubing 70, the output signal 210 of meter 206 will bewithin a predetermined bandwidth. An average value 212 of the signalwill be substantially constant. If the liner 34 fails, an electricallyconducting fluid 214, such as brine or water, may allow electricalcontact between the metallic layer 16 of the liner and the wellboretubing 70. Due to the electrical contact, indicated by event 216 in FIG.29, the average value of the signal 210 will decrease, indicating linerfailure to the wellbore staff at surface. In case of liner failure, theoperation of applying a liner to the wellbore tubing may be repeated,providing a second layer of liner 34 to the inner surface of the tubingto restore corrosion resistivity.

In an alternative embodiment, a liner may be comprised of any suitablematerial. The material may be a composite material as described above, asingle layer metallic material, a single layer polymer material, or anycombination thereof.

The liner 220 may be provided as a sheet material 222 in a first step,shown in FIG. 30.

In a second step, shown in FIG. 31, opposite sides 224, 226 of the sheetmaterial 222 may be bend upwards and toward each other, indicated byarrows 228 and 230. When the sides 224, 226 engage each other, they maybe interconnected. Interconnecting may be done by welding, by weldingdevice 232.

The resulting liner, shown in FIG. 32, may be flat. The liner 220 asshown in FIG. 32 can be reeled. The reel 130 may be ready for transportto a wellbore.

An embodiment of application of the liner in a wellbore is shown in FIG.33. The reel 130 comprising the reeled liner 220 is arranged on adrilling rig 240.

In a first step, an end of the liner 220 is provided with a plug 244.The plug 244 has a dimension substantially equal to an internal diameterof the wellbore tubing to the lined. In the example as shown in FIG. 33,the liner will be arranged on the inner surface of the production tubing70. The production tubing is arranged within a production casing 69. Theplug 244 will substantially plug the inner fluid passage of theproduction tubing 70.

In a second step, the plug 244, having the liner 220 attached to it, isintroduced in the top end of the wellbore tubular 70 (FIG. 33).

In a second step, a folding unit 246 is installed (FIG. 33). Saidfolding unit may comprise one or more rollers 248 for folding the liner220 in a predetermined form. Said predetermined form may be a C-shape incross-section.

In a third step, the plug 244, including the folded liner 250 which isattached to it, is pumped downhole. Herein, a fluid such as water ordrilling fluid, may be pumped into the wellbore tubular 70 via inlet252. Any fluid below the plug 244 can be pumped out of the wellbore viathe annulus 254 between the tubing 70 and casing 69, and via outlet 256(FIGS. 33 and 35).

When the plug has reached a predetermined location in the wellbore, forinstance the downhole end 260 of the tubing 70, the liner 220 is fixedat surface and the folding assembly 246 is removed.

Referring to FIG. 35, the liner 220 is then cut at surface, creating afree uphole end 262. The uphole end 262 of the liner is opened. The openend 262 is fixated using suitable connecting means 264.

In a next step, an expander tool 270 is introduced in the open upholeend 262 of the liner 220. The expander tool 270 may be pumped into theliner 220 to unfold the liner and press the unfolded liner in engagementwith the inner surface of the wellbore tubing 70 (FIG. 37). In anembodiment (FIG. 34), the expander tool may have a front section 272providing a nose or tip to guide the expander through the liner. Amiddle section may be provided with a ridge 274 having a diameter closeto the inner diameter of the wellbore tubing 70. The ridge diameter mayfor instance be in the range of about 99% to 99.9% of the inner diameterof the wellbore tubing. An aft end 276 may have a smaller diameter, toallow retrieval of the expander tool.

Optionally, the expander may be retrieved to surface after expansion theliner. Herein, the aft end 276 of the expander tool may be attached towireline to retrieve the tool. In an embodiment, the expander may becollapsible to simplify the retrieval.

In an embodiment, seals may be applied to the liner at selectedlocations along the liner (FIG. 38). For instance, one or more sealrings 280 may be introduced in the wellbore tubing 70 and positioned atpreselected locations along said tubing. For instance, a seal ring 280may be positioned at or near the downhole end 260 of the wellboretubing. Another seal ring may be positioned at a top end of the liner.Thus, the one or more seal rings 280 will provide an additional barrier,preventing wellbore fluids from entering between the liner 220 and theinner surface of the wellbore tubing 70.

Upon retrieval of the expander tool, the expander may expand the one ormore seal rings 280 at their respective locations. The expanded sealring 280 will be forced into the wellbore tubing, creating a sealsection 282 due to internal compressive residual stresses (FIG. 39). Thelatter may be regarded as autofrettage, a metal fabrication technique inwhich a pressure vessel is subjected to pressure, causing internalportions of the part to yield and resulting in said internal compressiveresidual stresses.

The liner can be pumped downhole relatively easily, as described above.The liner is relatively thin, for instance 1 mm or less. The thicknessof the liner may be in the range of about 200 to 800 μm, for instanceabout 0.5 mm. The folded liner 250 will, as a result, have a diametermuch smaller than the inner diameter (ID) of the wellbore tubular. TheID of production tubing is typically about 4 to 5 inch (about 10 to 15cm). The folded liner 254 by comparison may, in its collapsed state,have a diameter of less than 3 inch (7.5 cm), for instance 2 to 3 inch(5 to 7.5 cm). Engagement between liner and tubing 70 is minimal as aresult. Friction is therefore also relatively low, allowing easy run inof the liner.

FIG. 40 shows a drilling site 300. A truck 302 carrying a reel 130 andcorresponding reeling mechanism 304 is arranged at the site 300. Theliner 220 is unreeled in a flat form 306 and guided along a guidingstructure 308 into the wellbore 310. Folding mechanism 246 folds theliner into a C-shape 312. The C-shaped liner is introduced in thewellbore tubing 70.

Further downhole, or in a subsequent step, the liner 220 may expand inshape. The liner may expand from a partially expanded shape 314 to atubular shape 320. The expansion process may partially occur byelasticity of the liner. Alternatively, or in addition, the liner may beexpanded by introducing pressurized fluid and/or by moving an expanderthrough the liner, as described above.

The liner of the present invention may be any liner suitable for aparticular downhole condition. The liner may have one or more metalliclayers. The one or more metallic layers may be combined with one or morepolymeric layers, as described above. The one or more polymer layers maybe applied to the one or more metallic layers in any suitable way, forinstance by spray coating or extrusion coating. The above describedembodiments herein provide examples, but alternative methods tofabricate the liner may be used as well.

The liner material of the present invention and its application forlining tubing in a wellbore provides a relatively low-cost option whileproviding the superior corrosion resistance properties ofhigh-performance steel or solid CRA tubing. As the liner material canapplied to the tubing after installation thereof in the wellbore, theinner surfaces of the threaded connectors between pipe sections willalso be effectively protected against corrosion. The latter allows theuse of conventional, relatively low-cost threaded connectors, such asAPI approved carbon steel connectors.

Cost saving on production tubing, compared to required solid CRA tubing,may exceed 80%. The added liner is relatively thin, thus minimallylimiting the inner diameter of the borehole. The invention allows therehabilitation of older wells in case of souring, increase in water cut,etc.

The present invention is not limited to the above-described embodimentsthereof, wherein various modifications are conceivable within the scopeof the appended claims. For instance, features of respective embodimentsmay be combined.

It will be understood that the method and system according to theinvention may be used to insert a kilometres long corrosion and leakinhibiting liner downhole along at least a substantial part of thelength of an oil and/or gas production tubing from just above a SlidingSide Door (SSD) or Side Pocket Mandrel (SPM) to just below a Sub SurfaceSafety Valve (SSSV). The unlined upper and lower sections of theproduction tubing string above the SSSV and below the SSD and/or SPM maybe made of a Corrosion Resistant Alloy (CRA).

If the liner is installed within a production tubing string the expanderfor expanding and unfolding the liner may not be attached to a wirelineor Coiled Tubing (CT) assembly but may be delivered to the bottom of thetubing string by the liner itself. The driving force for pushing theexpander up through the tubing string may be hydraulic pressure fromcirculating the well via the annular space between the tubing string andsurrounding well casing.

The liner expander may be designed to self adjust its outercircumference to variations in the internal width of surrounding tubingstring. Because the tubing string is not plastically deformed, thevariations from production remain, and the expander and liner must beable to adjust to the variation (up to about 4 mm difference in internaldiameter for a commonly applied production tubing string). This may beachieved by using a leaf spring and/or by a rubber expander.

The expander may also be configured to preserve a residual compressionforce between the expanded liner and surrounding tubing string afterexpanding the liner, to ensure that despite elastic relaxation andspring back in the liner, a mechanical interference fit is achievedwithout plastically deforming the surrounding tubing string.

The top seal will be set at surface, also in a special tubing jointintended for this purpose.

If the liner is installed within a vertical or inclined tubing or casingstring, the liner may be provided with metal to metal seals surroundingan upper end and a lower end of the liner to ensure no production fluidcan enter between the production tubing and the liner. The lower endseal may be locked to a locking joint in the tubing string.

The corrosion resistant liner may be manufactured from a CorrosionResistant Alloy (CRA), such as nickel alloy C22, as a kilometres longflattened tube with a wall thickness between 0.3 and 0.7 mm. The curvedinner surfaces of the flattened and folded liner may be provided with agel or thick oil dope to prevent collapse of curves and creation ofvertical leak paths.

Protective coatings with thicknesses of a number of micrometres, such asan abrasion resistant layer on the inside of the liner to protect itagainst wireline interventions and the fluid adsorbing coating on theoutside, may be applied during manufacture and before folding of theliner and storage of the folded and flattened liner on a reeling drum.

The fluid absorbing coating will swell on contact with water and/orother fluids trapped between the expanded liner and tubing string andthereby absorb any free water which might remain in the annulus betweenthe liner and the surrounding tubing or casing string, and to preventany detachment of the liner from the surrounding liner and creation ofleak paths. Removal of water and other liquid pockets from the residualspace between the expanded liner and a vertical or inclined tubingstring is particularly relevant, since even isolated and both axiallyand circumferentially spaced small pockets of water and/or other liquidsmay, assisted by vibration and temperature fluctuations, slowly migratedownwards and coalesce into larger water and/or liquid pockets that mayentirely circumvent a lower part of the liner and result in linercollapse and/or its detachment from the tubing. In such case isolatedgas pockets may accumulate in a similar manner and migrate as enlarged,optionally annular, gas pockets upwardly towards an upper end of thetubing string.

The fluid absorbing coating may comprise a cross-linked acrylatepolymer, which is generally known as a Super Absorbent Polymer(SAP) orhydrogel or, in dry state, as “slush powder”, which can absorb an amountof fresh water of up to 500 times of its own weight in fresh water, andan amount of mildly saline water of up to 50 times of its own weight.

Super Absorbent Polymers (SAPs) are described in U.S. Pat. No. 7,144,980and are commonly made by polymerizing acrylic acid blended with sodiumhydroxide in the presence of an initiator to form a poly-acrylic acidsodium salt (sometimes referred to as sodium polyacrylate). This SAP isthe most common type of SAP made today.

The fluid absorbing coating may also comprise a sticky glue and/or otheradhesive to firmly bond the liner to the tubing or casing string andfurther inhibit collapse and/or detachment of the thin foil liner fromthe surrounding tubing or casing string.

What is claimed is:
 1. A method for lining a tubing string, comprises:providing a reeled flat folded liner; unreeling the reeled flat foldedliner in a flat form; folding the flat formed liner into a C-shape;inserting the C-shaped liner into a tubing string; and unfolding theC-shaped liner to expand the C-shaped liner against an inner surface ofthe tubing string; wherein the step of unfolding the C-shaped liner toexpand the C-shaped liner comprises: unfolding an end of the C-shapedliner; fixating the unfolded end of the C-shaped liner within the tubingstring; and pumping an expander tool and/or pressurized fluid throughthe C-shaped liner.
 2. The method of claim 1, further comprisingexpanding the C-shaped liner whereby the C-shaped liner expands from apartially expanded shape to a tubular shape.
 3. The method of claim 2,wherein expanding the C-shaped liner partially occurs by elasticity ofthe C-shaped liner.
 4. The method of claim 1, wherein the C-shaped lineris expanded by introducing pressurized fluid into the C-shaped liner. 5.The method of claim 1, wherein the C-shaped liner is expanded by movingan expander through the C-shaped liner.
 6. The method of claim 5,wherein a driving force for moving the expander through the C-shapedliner is hydraulic pressure.
 7. The method of claim 1, wherein theC-shaped liner has one or more metallic layers.
 8. The method of claim1, wherein the reeled flat folded liner comprises a ductile corrosionresistant metal with a wall thickness less than 1 mm.
 9. The method ofclaim 1, wherein the reeled flat folded liner has an outer surface whichis at least partially coated with a fluid absorbing coating, which isinduced to absorb fluid trapped between an inner surface of the tubingstring and an outer surface of the expanded C-shaped liner.
 10. Themethod of claim 1, wherein the tubing string is a tubing or a casingstring in an oil and/or a gas production well.
 11. The method of claim1, wherein the step of providing the reeled flat folded liner comprises:providing a sheet material; bending opposite sides of the sheet materialtoward each other into engagement; interconnecting the opposite sides ofthe sheet material with each other; and reeling the resulting reeledflat folded liner onto a reel.
 12. The method of claim 11, wherein saidinterconnecting the opposite sides of the sheet material is done bywelding.
 13. The method of claim 1, further comprising transporting thereeled flat folded liner to a wellbore.
 14. A system for lining a tubingstring, comprises: a reeled flat folded liner; a guiding structureconfigured to guide the reeled flat folded liner in a flat form to thetubing string after unreeling, said guiding structure comprising afolding mechanism to fold the flat formed liner into a C-shape prior tointroducing the flat formed liner into the tubing string, wherein theC-shaped liner is inserted into the tubing string; and means to unfoldand to expand the C-shaped liner against an inner surface of the tubingstring; wherein the means to unfold and to expand the C-shaped linercomprises an expander tool comprising a front section, a middle sectionand an aft end, wherein the front section provides a nose or a tip toguide the expander through the C-shaped liner; and where the middlesection is provided with a ridge having a diameter close to an innerdiameter of the tubing string, wherein the aft end has a smallerdiameter to allow retrieval of the expander tool, wherein the aft end isattached to a wireline tool to retrieve the expander tool.
 15. Thesystem of claim 14, wherein the reeled flat folded liner is carried on atruck.
 16. The system of claim 15, wherein said truck further comprisesa reeling mechanism.
 17. The system of claim 14, wherein the expandertool self-adjusts its outer circumference to variations in internalwidth of the surrounding tubing string.
 18. The system of claim 14,wherein the tubing string is a tubing or a casing string in an oiland/or a gas production well.
 19. A method for lining a tubing string,comprising: providing a reeled flat folded liner; unreeling the reeledflat folded liner in a flat form; folding the flat formed liner into aC-shape; inserting the C-shaped liner into a tubing string; andunfolding the C-shaped liner to expand the C-shaped liner against aninner surface of the tubing string; wherein the folded liner has anouter surface which is at least partially coated with a fluid absorbingcoating, which is induced to absorb fluid trapped between an innersurface of the tubing string and an outer surface of the expandedC-shaped liner.
 20. A system for lining a tubing string, comprising: areeled flat folded liner; a guiding structure configured to guide thereeled flat folded liner in a flat form to the tubing string afterunreeling, said guiding structure comprising a folding mechanism to foldthe flat formed liner into a C-shape prior to introducing the flatformed liner into a tubing string; inserting the C-shaped liner into thetubing string; means to unfold and to expand the C-shaped liner againstan inner surface of the tubing string; and connecting means to fixate anopen end of the C-shaped liner within the tubing string; wherein themeans to unfold and to expand the C-shaped liner comprises: an expandertool; and a pump configured to pump the expander tool through theC-shaped liner.
 21. The system of claim 20, wherein the expander toolcomprises a front section, a middle section and an aft end, wherein thefront section provides a nose or a tip to guide the expander through theC-shaped liner; and where the middle section is provided with a ridgehaving a diameter close to an inner diameter of the tubing string. 22.The system of claim 21, wherein the expander tool further comprises anaft end that has a smaller diameter than the middle section, to allowretrieval of the expander tool.
 23. The system of claim 22, wherein theaft end is attached to a wireline tool to retrieve the expander tool.24. The system of claim 20, wherein the tubing string is a tubing or acasing string in an oil and/or a gas production well.